PAGE : 185/ 195

CERTIFICATO DI COLLAUDO EN 10204/3.1 1546708 PAG. /

SPECIFICATION:
ASTM A 240 ASTM A 480 CUSTOMER ORDER № CUSTOMER

ASME SA 240
INTERNAL ORDER № 8E150236
MILL TEST CERTIFICATE
DOC.CREDIT N. M04091506NU00250
PRODUCT: SHIPPING NOTICE № 00056352
STAINLESS STEEL COILS

CHEMICAL COMPOSITION STELL TYPE:

COIL, N* HEAT N* 316L/316
%C % Mn % SI %P %S % Cr % Ni % Mo %N % Ti % Cu % %
316L

760819 0442576 .023 .930 .340 .027 .001 16.54 10.14 2.04 .046 .240
833344 0490070 .023 .890 .320 .028 .001 16.82 10.24 2.04 .048 .220
PRODUCER TRADE MARK

INSPECTOR STAMP:
THE MATERIAL MEETS THE HARDNESS REQUIREMENTS OF NACE MR0175/MR0103
80 CENTRO Dl FINITURA P.F, TERN 1050 °c M04091506NU00250
HEAT TRATEMENT – ANNEALING: AIR – WATER SPRAY – WATER COOLING STEELMAKING PROCESS THE MATERIAL IS RESISTANT TO INTERCRYSTALLINE CORROSION IN DACCORDANCE WITH: ASTM A262 E
2
TEST RESULTS (1 N/mm = 1 M Pa)
TRACTION
HARDNESS BEND GRAIN
Rp 02% Rp 1% Rm A%
DIMENSIONS
PRELIEVD

PACKAGE N* COIL N* P-CES N* FINISH WEIGHT

mm
SENC

(1) (2) N/mm2 N/mm2 N/mm2 Lo=2” Lo=80 Lo=A5 HR B H 180 (mm)
REQUIRED CHARACTERISTICS ≥ 170 ≥ >485 ≥ 40 ≥ ≥ ≤ 95 ≤
C22741 760819 1 . 50X1545 . 0 1 2B 8730 T T 275 607 57 . 3 75 . 0
C22741 C T 269 598 58 . 4 73 . 0
C22742 760819 1 . 50X1545 . 0 1 2B 9020 T T 275 607 57 . 3 75 . 0
MOD. 2114-33355130

C22742 C T 269 598 58 . 4 73 . 0

C34909 833344 1 . 50X1245 . 0 1 2B 6048 T T 266 589 58 . 8 73 . 0
C34909 C T 264 585 59 . 3 72 . 0
C34921 833344 1 . 50X1245 . 0 1 2B 4983 T T 266 589 58 . 8 73 . 0
C34921 C T 264 585 59 . 3 72 . 0

We certify the products rated above complying order requirements.

COMPLIES WITH ED 2000/53/EC

1)Location 2) Direction MARKING

T = Top T- Transverse
Wn – Type
Heath –Coll N
Certificato emesso automaticamente
C = Bottom L - Long Thinkness - Flash TERNI.II 08-07-2015
 PAGE : 194/ 195

Mill Test Certificate

Certificate No.:
Seller: Date of issue:
Manufacturer: Surface Finish:
Order No.: PO No.:
Supplier: Commodity: STAINLESS COLD ROLLED COIL
Customer: Spec & Type: ASTM-A240M-316L
Tensile Test Chemical Composition

Position

Division
Weight Hardness
YS 02 TS EL C Si Mn P S Cr Ni Cu Mo N
Size Product No. Quantity (kg) Heat No.
HRB
(%) (%) (%) (%) (%) (%) (%) (%) (%) (ppm)

0.8×1219×C QCR0430 1 14.579 SY80601 T 289 644 55 60.0 L 0.0203 0.579 1.036 0.0311 0.0039 16.208 10.070 0.245 2.056 256
B 301 642 55 60.1

*** Sub Total (030)*** 1 14.579 (kg)

** Heal Treatment ** Solution Treatment Min 1040 °C Quenching

*** Grande Total*** 1 14.579 (kg)

*** Grand Total *** 1 14.579 (kg) *** Last Item***

* Position - T: Top, Middle, B: Bottom We hereby certify that the material herein has been made in accordance with the order and above specification.
* Tensile Test. Direction: Transversal, Gauge Length: 50 mm (Rectangular) No repair welding was performed to the products.
YP Method: 0.2% off-set Test Certificate is Issued according to EN10204 3.1.
* Division – L: Ladle Analysis

Legal sanction can be imposed on forging. Improper use of product can cause safety issues._
Surveyor To:

<PAGE 1> MANAGER OF QUALITY ASSURANCE TEAM

 PAGE : 194/ 195

MILL TEST CERTIFICATE EN 10204 3.1

End User Works No. Certificate Ref. No.

141112010 20150107-1026-1-013 1/4
Customer Name Purcharge Order No.

Specification Sub-Section Grade (TYPE) Edition Addenda UNS Finish

ASTM A240M/48OM 304 S30400 No. 1

Head Treatment – Solution Annealed Condition of Plate Mps No.

1080 °C WATER COOLING GOOD
Intergranular Corrosion Test UT Test Spec

Product SIZE Per Impact Test (charpy)

DIR S
(mm) me V-notch °C Min J
Request Q`ty Weight Rough POSIT EC I
No. Bungle No. Heat No. Plate No. AGS abili
No. (sh) (kg) ness ION TIO Z
T W L ty 1st 2nd 3rd Avg
N E
(u)
T
1 SD10586 11P8644878-1-01 35 2.438 7.000 1 4.820.0
B
T
2 SD10586 11P8644878-1-02 35 2.438 7.000 1 4.820.0
B
T
3 SD10570 11P8644899-1-01 25 2.000 6.096 1 2.460.0
B
T
4 SD10570 11P8644899-1-02 25 2.000 6.096 1 2.460.0
B
T
5 SD10570 11P8644901-1-01 25 2.000 6.096 1 2.460.0
B
Sub Total 5 17.020.0 Grand Total 18 49.508.0
D Tensile Test (1N/m=1MPa)
D P
I G Hard
No. I Chemical Composition (%) Practice O
R L Y.S Y.S
V S T.S EL Ra ness
I I
E 0.2% 1.0%
Cont C Si Mn P S Cr Ni Mo N Co Cu Ti Nb C N/mm2 % HRB
S T
T
I Max 0.070 0.75 2.00 0.045 0.030 19.50 10.50 0.100 I 92
O A E B C I
O %
O
n Min 17.50 8.00 N
N
205 515 40
L T
1 0.066 0.48 0.96 0.030 0.002 18.42 8.10 0.18 0.034 0.18 0.29 C E 258.3 322.3 653.7 57.0 81.5
P B
L T
2 0.066 0.48 0.96 0.030 0.002 18.42 8.10 0.18 0.034 0.18 0.29 C E 258.3 322.3 653.7 57.0 81.5
P B
L T
3 0.050 0.48 0.97 0.031 0.002 18.10 8.05 0.19 0.032 0.16 0.34 C E 242.8 306.2 646.5 54.9 79.3
P B
L T
4 0.050 0.48 0.97 0.031 0.002 18.10 8.05 0.29 0.34 C E 242.8 306.2 646.5 54.9 79.3
P B
L T
5 0.49 0.49 0.98 0.031 0.001 18.20 0.19 0.038 0.16 0.34 C E 255.9 316.3 652.1 54.9 60.4
P B

Remarks

Manufacture Info.
NO REPAIR WELDING HAS BEEN PERFORMED ON THE MATERIAL Boneyer or Inspector to:

Position T: Top N: Middle B: Bottom Division L: Ledle Analysis P: Product Analysis

N Direction L: Longitudinal C: Crossfire (Transverse) AGS ASTM E112 A, G, S TEST
o GL (Gauge Lengh) ASTM E8 10% Oxalic Acid Etch Text – ASTM A262 Practice A General Manager of DKC Quality
t Rectangle : A: 50mm B: 70mm C: 100 mm D: 5.65VA 1: Step Structure 2: Dual Structure
Round : E: 50mm F: 70mm G: 5.65VA 3: Ditch Structure 4: Isolated Ferrite Roots
e
Impact Test Specimen Size 5: Interdendritic Ditchs 6: End Grain Pilling 1.11
1:10X10mm 2:7.5x10mm 3:5.0X10mm 4:2.5X10mm CU-CU Sulfate-Sulfuric Acid TEST – ASTM A262 Practice E
(1:0.39X0.39 2:0.3X0.39 inch 3:0.2X0.39 inch 4:0.1X0.39 inch G: GOOD N: NOT GOOD
inch
We hereby certify that the material herein has been made in accordance with the order and specification

F21S-01(A4) x Rev.6(2011.07.27)
 PAGE : 194/ 195

INSPECTION-CERTIFICATE

CUSTOMER :
SUPPLIER : CERT. NO. :
PURCHASE ORDER NO : MANUFACTURE NO. :

STEEL GRADE : 304/304L SPECIFICATION: ASTM A479MOD MELTING PROCESS : E.A.F.

SIZE: DIAMETER 150 MM EDITION/ADDENDA: 14 V.O.D.
ARTICLE : ROUND BARS STATE OF DELIVERY : SOLUTION TREATMENT STRAND CASTING
ROUGH TURNED

Chemical Composition(wt.%) Non-Metallic Inclusion Test

Heat No.
C Si Mn P S Ni Cr Mo Cu
MIN. 8.000 18.000 ASTM-E45
Spec.
MAX. .030 1.000 2.000 .0450 .0300 10.500 20.000 TA TB TC TD HA HB HC HD
N08703 .009 .414 1.602 .0337 .0234 8.547 18.024 .202 .567 2.0 0.0 1.5 1.0 0.0 0.0 0.0 0.0
Tensile Properties Hardness Impact Test Decarburized Grain Additional Tests
Test No.
Y.S.(KSI) T.S. EL. R.A. Body Depth (mm) Size Ultrasonic test: GOOD
(Lot No.)
0.2% (KSI) (%) (*) HB TOTAL FERR. No.
MIN. 30.0 75.0 30.0 40.0
Spec.
MAX.
4000-1 41.0 79.0 63.0 78.0 135 2.0

Number Weight
Lot No. Bundle No. Length (ram) Additional Tests / Remarks
of Qt. Kg lb
5041194000 50411940001 5785 - 5895 2 1.648 3.633 Corrosion Test: GOOD
Solution : 1050°C. 3:00Hrs. WATER cooling

ISO 15156 (Hardness Only)

EN 10204 Type 3.1 /NO REPAIR WELDING. FREE FROM MERCURY CONTAMINATIO

We here certify, that the material described above has been

tested and complies with the terns of the order contract.
Our quality system is certified in accordance with Team Manager. Quality Assurance Team
TOTAL 2 1.648 3.633 ISO 9O0I: 2008 by DNV. DATE : JUN.01. 2015