MAT 1210 MCGB - Data Sheet For Suppliers Old MAT No.: 121

This document provides specifications for carbon steel plate materials used for pressure vessels. It lists the chemical composition requirements, mechanical properties at room temperature, applicable standards, and contact information. The plate has a tensile strength over 400 MPa, is hot rolled for medium temperatures, and complies with EN 10028-2 for pressure vessel steel. Dimensions range from 0-250 mm thick, with specified chemical element percentages and mechanical properties that vary with thickness.

Uploaded by

Mohamed
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
186 views1 page

MAT 1210 MCGB - Data Sheet For Suppliers Old MAT No.: 121

This document provides specifications for carbon steel plate materials used for pressure vessels. It lists the chemical composition requirements, mechanical properties at room temperature, applicable standards, and contact information. The plate has a tensile strength over 400 MPa, is hot rolled for medium temperatures, and complies with EN 10028-2 for pressure vessel steel. Dimensions range from 0-250 mm thick, with specified chemical element percentages and mechanical properties that vary with thickness.

Uploaded by

Mohamed
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

MAT 1210

MCGB - DATA SHEET FOR SUPPLIERS Old MAT No.: 121, -, -


Pressure Vessel Plate, Carbon Steel

For more information contact FLSmidth

PROPERTIES:
Hot rolled boiler plate, wide flats and shapes for medium temperatures.
Tensile strength Rm > 400 MPa.

STANDARDS:
General requirements:
When reference to this MAT NO appears on FLS Drawing or FLS Parts List or in FLS Purchase Order the
data from the Primary Standard is used as acceptance criteria.

Specific deviations in requirements made in the FLS Parts List, the FLS Purchase Order or a FLS
Instruction always overrules this data sheet.

Alternatively accepted International Standards listed in this sheet may be used if the suppliers
documentation covers at least the documentation required in the Primary Listed Standard. This means that
supplementary tests in some cases will be necessary.

Primary Standard:
EN 10028-2 (2009), MATERIAL: P 265 GH, MATERIAL No.: 1.0425
Flat products made of steel for pressure purposes - Part 2: Non-alloy and alloy steels with specified
elevated temperature properties

CHEMICAL COMPOSITION:
% C max or % Si max or % Mn max or % P max or % S max or % N max or % Al min or
Dim. mm
range range range range range range range
0-6 0.20 0.40 0.60-1.40 0.025 0.010 0.012 0.020
6- 0.20 0.40 0.80-1.40 0.025 0.010 0.012 0.020

% Cr max % Mo max or % Ni max or % V max or % Nb max or % Ti max or % Cu max % Other max


Dim. mm
or range range range range range range or range or range
0-6 0.30 0.08 0.30 0.02 0.020 0.03 0.30
6- 0.30 0.08 0.30 0.02 0.020 0.03 0.30
%Cr+%Cu+%Mo+%Ni less than 0.70%

MECHANICAL PROPERTIES AT ROOM TEMPERATURE:


Tensile Imp.
Yield Strength Elong. M.Elas
Strength Area Reduction Hardness Energy KV,
Condi- Dim. MPa % GPa
MPa Min
tion mm
Rm Re A5 Z Z E HRc HB HV °C J
N 0-16 410-530 265 - 22 - - - - - - -20 27
N 16-40 410-530 255 - 22 - - - - - - -20 27
N 40-60 410-530 245 - 22 - - - - - - -20 27
N 60-100 410-530 215 - 22 - - - - - - -20 27
N 100-150 400-530 200 - 22 - - - - - - -20 27
N 150-250 390-530 185 - 22 - - - - - - -20 27
N: Normalised. Values of Creep Stress and Creep Strength have a scatter band of +-20%. Yield Strength at elevated
temperatures for dimensions less than 150 mm are up to 20% higher.

Rev_No : 11,0 Issue Date: 01-06-1998 Prepared by: BKL


Revision Date: 12-06-2014 Approved by: KHN Page 1 of 3