Examination Results: Phateco

This document summarizes the magnetic particle inspection of weld MT.PL02.T15 on a C-S material pipe. The inspection was performed according to ASME BPV Section VIII standards using a yoke magnetization method. Two linear indications measuring 40mm and 5mm were found and evaluated as acceptable based on the acceptance criteria. The inspection was repeated after applying coating layers, with the same two indications found and accepted each time.

Uploaded by

Sang Nguyen Quang
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
53 views1 page

Examination Results: Phateco

This document summarizes the magnetic particle inspection of weld MT.PL02.T15 on a C-S material pipe. The inspection was performed according to ASME BPV Section VIII standards using a yoke magnetization method. Two linear indications measuring 40mm and 5mm were found and evaluated as acceptable based on the acceptance criteria. The inspection was repeated after applying coating layers, with the same two indications found and accepted each time.

Uploaded by

Sang Nguyen Quang
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

Report No. : L691.DEMO.

MT01

Date : 30.12.2015

Page : 1 of 2
CLIENT CODE or STANDARD : ASME BPV Sec. VIII Div.1 Edition 2015
PROJECT ACCEPTANCE CRITERIA : ASME BPV Sec. VIII Div.1 Appendix 6
LOCATION : THAI BINH 2 SITE NDT EXTENT : 100%
ITEM : PROCEDURE : Rev. : 0
MATERIAL : C-S PRODUCT TYPE
SKETCH : See attached PROCESS
Equipment Used S/N : NW1309151 Next Cal. Due : 27/03/2016
Examination Method Continuous Residual
Magnetizing Method Permanent Yoke Yoke Prod
Current/Lifting Power AC DC Lifting power (Min. 4.5 kg)
Magnetic Particle (Brand) Contrast paint (Brand)
Medium Dry Wet Fluorescent Visible Contrast
Prepared edge After Welding After PWHT
State of Examination
Base Metal After Repair In-service
Type of joint Butt joint Tee-joint Corner-joint Lap-joint
Surface Condition Brushing As welded As forged As grinded
o
Surface Temperature Ambient (17.6 C)
Lighting Condition Day light Artificial Black Light Light intensity (lux): 1013~6716
Lighting Meter : Kyoritsu 5202 Serial : N1001410 Next Cal. Due : 30/06/2016
Yoke Distance : min 75mm to max 160 mm
Examination sequences Two Perpendicular direction One Direction Other
Demagnetization Yes No Post Cleaning Yes No
EXAMINATION RESULTS
THICK- WELDED INSP. INDICATION EVALUATION DATE OF
WELD IDENTIFICATION NESS LENGTH LENGTH LENGTH LOCATION INSPECTION REMARKS
(mm) (m) (m) No TYPE ACC. REJ. (dd/mm/yy)
(mm) (mm)
MT.PL02.T15 (Side B) 14 0,28 0,28 1 L 40 O…111  30/12/2015 After 2 layers coating

" " " " 2 L 5 O…156  '' "


" " " " 1 L 40 O…111  '' After 4 layers coating

" " " " 2 L 5 O…156  '' "


" " " " 1 L 40 O…111  '' After 6 layers coating

" " " " 2 L 5 O…156  '' "

TOTAL INSPECTED LENGTH: 0,28 M


Legend: ACC: Accepted REJ: Rejected L: Linear indication Ro: Round indication