PROPERTY DATASHEET
NYLON 630G
Black PA 6
30% Glass Reinforced Polyamide – Injection Molding Grade
NYLON 630G (AASCEND)
Black PA 6
30% Glass Reinforced Polyamide – Injection Molding Grade
Properties Value Unit Method
PHYSICAL PROPERTIES
Density 1.35 g/cm3 ISO1183
Water absorption (24 hr, 23°C) 2.0 % Sim. to ISO 62
Humidity absorption (23°C, 50% RH) 6.5 % Sim. to ISO 62
MECHANICAL PROPERTIES
Tensile modulus (at 1mm/min) 8000 MPa ISO527-1
Stress at break (at 5mm/min) 120 MPa ISO527-1
Strain at break (at 5mm/min) 3.8 % ISO527-1
Charpy notched impact strength (at +23ºC) 8 KJ/m² ISO179/1eA
Charpy unnotched impact strength (at +23ºC) 45 KJ/m² ISO179/1eU
Izod notched impact strength (at +23ºC) 7 KJ/m² ISO180/1eA
Izod unnotched impact strength (at +23ºC) 40 KJ/m² ISO180/1eU
THERMAL PROPERTIES
Heat deflection temperature (at 1.8 MPa) 210 ºC ISO75-2
Heat deflection temperature (at 0.45 MPa) 220 ºC ISO75-2
Coff. Of. Lin. Therm. expansion in direction of flow 0.2 E-4/K ISO11359-1/-2
Coff. Of. Lin. Therm. expansion Perpendicular to flow 0.7 E-4/K ISO11359-1/-2
PROCSSING CONDITIONS FOR TEST SPECIMENS
C injection moulding – melt temp. 260 ºC ISO294
C injection moulding – mould temp. 80 ºC ISO294
PROCESSING RECOMMENDATION
Drying temperature dry air dryer 80 ºC -
Drying time dry air dryer 2-6 h -
Residual Max moisture content 0.03-0.15 % Acc.to karl fischer
Melt temperature (Tmin-Tmax) 250-280 ºC -
Mold temperature 80-100 ºC -
Grade B 6 GF35 BK (AUTOTECH)
Polyamide 6
30% Glass Reinforced Polyamide – Injection Molding Grade
Properties Method Unit Method
PHYSICAL PROPERTIES
Density at 23°C 1.4 g/cm3 ISO 1183
Mould Shrinkage (%) 0.2 - 0.5 % INTERNAL
Filler Content (1h/600°C) 35 % ISO 3541
MECHANICAL PROPERTIES
Flexural Modulus (23°C - 2 mm/min) 9000 MPa ISO 178
Izod notched impact strength (23°C) ISO 12 KJ/m² ISO 180/1A
Tensile stress at break (23°C-5 mm/min) 150 MPa ISO 527-2
Tensile elong. at break (23°C-5 mm/min) 3 % ISO 527-2
THERMAL PROPERTIES
HDT, A (1.80 MPa) 205 °C ISO 75/Ae
Flammability
PROCESSING RECOMMENDATION
Flammability class (3,0 mm) HB UL94
Glow Wire Flammability Index GWFI (3,0 650 °C IEC 606925-2-
mm) 12
All Information supplied by or on behalf of company in relation to its products, whether in the nature of data, recommendations or otherwise, is supporte
but company assumes no liability whatsoever in respect of application, processing or use made of the aforementioned information or products, or an
undertakes all liability in respect of the application, processing or use of the aforementioned information or product, whose quality and other properties
thereof. No liability whatsoever shall attach to Company for any infringement of the rights owned or controlled by a third party in intellectual, industrial
application, processing or use of the aforementioned information or products by the buyer