Sheet No.
: 4 0 5 2 - K
Issued Date : Jan. 2023
ACRI 800 FINISH HS
(ACR 800 F HS)
PRODUCT DESCRIPTION
ACRI 800 FINISH HS is an acrylic paint designed for use as a finish coat of which paint film is formed by
evaporation of solvents. The coating has excellent adhesion property and weathering resistance, with
superior gloss and color retention.
PRODUCT INFORMATION
Type Acrylic finish paint
Recommended Use Finishing coat on ship's topside, boot top, deck, superstructures
Type of binder Acrylic resin
Color White, As specified
Flash Point 22.1 ℃
Solids by Volume 54% ± 2 (Test Method : ISO-3233)
VOC 422 g/ℓ (Method24), 441 g/ℓ (Korea Clean Air Conservation Act)
Coverage(Theoretical) 15.00 ㎡/ℓ [0.065 ℓ/㎡] at D.F.T 35㎛
Wet Film Thickness 56 - 74 ㎛
Dry Film Thickness 30 - 40 ㎛
Drying Time Temperature 5℃ 10℃ 20℃ 30℃
(at D.F.T. 35㎛) Set-to-touch 1 hr. 50 mins 30 mins 30 mins
Hard Dry 6 hrs. 5 hrs. 4 hrs. 3.5 hrs.
Painting Interval Minimum 6 hrs. 5 hrs. 4 hrs. 3.5 hrs.
(at D.F.T. 35㎛) Maximum - - - -
Thinner RAVAX THINNER, CR/ACRI THINNER A, CR/ACRI THINNER C
Method of Application Airless spray, Brush, Roller
Temperature : Minimum 0℃
Humidity : Maximum 85 % R.H.
For Airless spray ;
Condition of Application
Tip No. : GRACO 515, 615, 715
Paint output pressure : 11.7 – 14.7 MPa
Viscosity : 2dPa∙s
Preferable Preceding Coats BANNOH series, BANNOH 1500 R Z, UMEGUARD SX Series, etc.
Preferable Subsequent Coats -
Packaging One pack product
Notes :
1. Adequate ventilation must be maintained during application until it reaches hard dry in order to fully evaporate the
solvents.
2. Do not add thinner exceeding maximum amount of VOC in each local regulation.
3. Control the wet film thickness within 200㎛ in a single coat to avoid unpredictable defects such as blistering, cracking
and peeling.
4. Do not apply ACRI 700 FINISH ST on top of the ACRI 800 FINISH HS to avoid cracking.
The information given in this sheet is effective at the date shown above and subject to revision from time to time without notice.