Product Information
ABP-2030
Mineral Reinforced PP
FEATURES APPLICATIONS
PP+ EPDM-TD22 Injection molding
Excellent stiffness/Impact balance Automobile Part
Good flowability properties Bumper
Automobile exterior parts
S.I.
Properties[1] Test Standard Test Condition S.I. Unit
Typical Value[1,2]
Mechanical
Tensile Strength ISO 527 50mm/min MPa 18
Elongation at break ISO 527 50mm/min % 50
Flexural Strength ISO 178 2mm/min MPa 25
Flexural Modulus ISO 178 2mm/min MPa 1950
2
Izod notched impact strength ISO 180 23℃ kJ/m 30
Thermal
Temperature of Deflection Under Load ISO 75-2 1.8MPa ℃ 53
Others
Density ISO 1183 -- g/cm3 1.06
Ash Content ISO 3451/1 -- % 22
Melt mass-flow rate(MFR) ISO 1133-1 230℃/2.16kg g/10min 30
Mold Shrinkage KINGFA 23℃ % 0.6-0.9
Flammability ISO 3795 3mm mm/min 45
[1] These are typical values of the product’s properties, and these values alone do not represent a sufficient basis for any part
design and are not intended for use in establishing maximum, minimum, or ranges of values for specification purposes.
[2] The listed values are maybe different for pigmented material.
http://www.kingfa.com.cn Update： 4/14/2020
NOTICE: The data contained in this publication are based on our current knowledge and experience. This information may be
subject to revision without informing in advance as new knowledge and experience become available. Because use conditions and
applicable laws may differ from one location to another and may change with time, Customer is responsible for determining
whether products and the information in this document are appropriate for Customer’s use and for ensuring that Customer’s
workplace and disposal practices are in compliance with applicable laws and other governmental enactments. Seller assumes no
obligation or liability for the information in this document. NO WARRANTIES ARE GIVEN; ALL IMPLIED WARRANTIES OF
MERCHANTABILITY OR FITNESS FOR A PARTICULAR USE ARE EXPRESSLY EXCLUDED.
Product Information
ABP-2030
Typical Processing Conditions
Optimum Range
Melt Temp. 220℃ 190-240℃
Barrel Zone Temp. Rear 190℃ 180-200℃
Center 210℃ 200-220℃
Front 220℃ 210-240℃
Mold Temp. 30℃ 20-50℃
Processing Temp. Upper Limit 260℃
Injection Speed Moderate to high
Pre-dry Requirements 80-100℃, 2~4hr
The parameter is just for referential purpose only. In actual processing, the parameter should be adjusted by
construction of mold, shape and size of product, and so on.
SAFETY AND HANDLING CONSIDERATIONS
Material safety data sheets (MSDS) for resins are available recommended
from Kingfa Sci. & Tech. Co. Ltd. and its subsidiaries. MSDS Good general ventilation of the polymer processing area is
sheets are provided to help customers satisfy their own recommended. Processing may release fumes which may
handling, safety, disposal needs, and those that may be include polymer fragments and other decomposition products.
required by locally applicable health and safety regulations. Fumes can be irritating. At temperatures exceeding melt
The following comments are general and applied only to temperature, polymer fragments can occur. Good general
resins as supplied. Various additives and processing aids ventilation should be sufficient for most conditions. Local
used in fabrication and other materials used in finishing steps exhaust ventilation may be necessary for some operations.
have their own safe use profile and must be investigated Use chemical splash goggles if there is a potential for
separately. exposure to particles which could cause injury to the
These resins have a very low degree of toxicity under normal eye. Use gloves with insulation for thermal protection.
conditions of use and should pose no unusual problems from Color change of the product may be caused by UV exposure
ingestion, eye, or skin contact. However, caution is advised in general. So it is recommended that storage should keep in
when handling, storing, using, or disposing of these resins. dry, cool place and avoid direct sunlight
Good housekeeping and controlling of dusts are necessary for We encourage customers and potential users of our products
safe handling of product. Workers should be protected from to review their applications for such products from the
the possibility of contact with molten resin during fabrication. standpoint of human health and environmental quality. To
Handling and fabrication of plastic resins can result in the help ensure that our products are not used in ways for which
generation of vapors and dusts. Dusts resulting from sawing, they were not intended or tested, our personnel will assist
filing, and sanding of plastic parts in post-molding operations customers in dealing with ecological and product safety
may cause irritation to eyes and the upper respiratory tract. In considerations. Your sales representative can arrange the
dusty atmospheres, using an approved dust respirator is proper contacts.
http://www.kingfa.com.cn Update： 4/14/2020
NOTICE: The data contained in this publication are based on our current knowledge and experience. This information may be
subject to revision without informing in advance as new knowledge and experience become available. Because use conditions and
applicable laws may differ from one location to another and may change with time, Customer is responsible for determining
whether products and the information in this document are appropriate for Customer’s use and for ensuring that Customer’s
workplace and disposal practices are in compliance with applicable laws and other governmental enactments. Seller assumes no
obligation or liability for the information in this document. NO WARRANTIES ARE GIVEN; ALL IMPLIED WARRANTIES OF
MERCHANTABILITY OR FITNESS FOR A PARTICULAR USE ARE EXPRESSLY EXCLUDED.