ESTABLISHED IN 1959 CONSTRUCTION CHEMICALS

Waterproofing Applications
Contents

Waterproofing of flat roofs...................................................................................................4

Waterproofing of walkable roofs using hybrid waterproofing coating..........................................4

Waterproofing of walkable roofs using cementitious elastic system...........................................6

Waterproofing of pools, balconies and tanks......................................................................7

Waterproofing of pools using cementitious elastic system.........................................................7

Waterproofing of underground walls...................................................................................8

Waterproofing of underground walls with crystalline cementitious mortar..................................8

Interior waterproofing of underground walls with high strength cementitious mortar..................9

Waterproofing of facades....................................................................................................10

Waterproofing of vertical surfaces using waterproofing coatings with thermal insulating properties......10

Auxiliary products................................................................................................................12

Other waterproofing products............................................................................................13

Indicative applications of NEOTEX® waterproofing systems...........................................14

Products chart......................................................................................................................15

2
NEOTEX® SA is constantly and successfully developing special- because of poor technical maintenance, have an effect on the
ized waterproofing solutions. Thanks to its expertise and long structures. When these appear, the poor quality of the air inside
experience, NEOTEX® is highly appreciated by the whole range the rooms, the thermal discomfort, the increased humidity, are
of its customers, from the technical world to the end users. By some of the major side effects. Thus, having a successful wa-
providing accurate solutions with the use of the appropriate ma- terproofing, insulation and proper maintenance with NEOTEX®
terials, NEOTEX® is established in the customers’ conscious- products, the structural elements of construction are protect-
ness as a company with reliability, knowledge and experience in ed by a remarkable way, therefore improving the quality of in-
the very broad field of waterproofing. habiting.

For the selection of the appropriate solution in terms of cost-effi- The most common reasons of waterproofing problems are:
ciency, thorough inspection of the problem is needed, assessing manufacturing defects, improper application, improper use of
the reasons of causing it and taking into consideration the differ- materials during the construction, the maintenance, the repair
ent conditions of each case, in order to avoid future recurrenc- and the expected natural deterioration of the construction.
es. NEOTEX® SA, having foreseen the market trends, utilized its
expertise in waterproofing & insulation systems since 1959 and Whenever waterproofing problems appear, we must mainly ex-
offers a full range of modern systems to meet any requirements amine the source of the humidity, the path it follows, the form it
of the today’s construction sector. appears in (vapor, liquid, condensation of water vapor), and the
reason that cause it for instance capillary or other crack, water
The adequate waterproofing and insulation of all constructions vapor, air pressure, gravity. In many cases, its existence is obvi-
are issues of great importance. The problems that stem from ous and easily recognizable. But there are problems that are not
the insufficient and incomplete waterproofing - insulation or visible so research to identify them is needed.

3
WATERPROOFING OF FLAT ROOFS
The surface, the current conditions, the extent of the area, the future use etc., influ-
ence the way we treat the problem. Depending on each individual case we select the
appropriate materials.

WATERPROOFING OF WALKABLE ROOFS USING HYBRID WATERPROOFING COATING

Neoroof®
Hybrid waterproofing coating for roofs (UV-curable) of high solar reflectance
and emittance providing thermal-insulating properties
Hybrid, waterproofing coating for roofs with UV cross linking system. It is certified product, with high reflectance
and total emittance providing thermal insulation. It forms a non-penetrating against moisture film with resistance
to extreme low temperatures down to -35oC.

P R O P E R T I E S & A D VA N TA G E S F I E L D S O F A P P L I C AT I O N

`` Hybrid waterproofing coating for roofs with thermal insulating prop- `` Roofs made of concrete, cement boards, mosaic, cement slurries
erties. `` Rooftops with resistance to stagnant water
`` It creates a thin elastic watertight membrane for walkable rooftops `` Mineral bitumen membranes
with resistance to stagnant water. `` Metallic surfaces
`` UV curable. After 2 days exposure to direct sunlight the film is not tacky `` Next to and under photovoltaic panels, enhancing their efficiency
even under high temperatures and simultaneously maintains its elas- `` Air-conditioning tubes
ticity between -35°C and +80°C, offering excellent impermeability to `` New or old polyurethane waterproofing layers
water `` Thermal-insulating polyurethane panels and polycarbonate panels
`` Certified with CE according to EN 1504-2 `` Galvanized metal sheets and bituminous membranes with aluminium
`` It covers capillary cracks and provides total protection against moisture sheet surface
`` It prevents the deposit of dust and pollutants, retaining the whiteness, `` Over old roofing made of asbestos
thermal-reflectance properties and smooth surface (Upon some surfaces above, it is necessary to prime them with the appropriate
`` Economic and easily applied with high spreading rate each time primer, before Neoroof® application)
`` Water-based, one component, friendly to the end-user and the envi-
ronment
`` It contributes to the transpiration of the building, resulting to the dehy-
dration of the interior areas and the improvement of the thermal con- TECHNICAL CHARACTERISTICS
ditions and comfort
`` Appearance: White, viscous liquid
`` It reduces the surface temperature of the bituminous membrane, de-
`` Density (ISO 8962): 1,30 g/cm3
laying the aging and combined with Revinex® stabilizes the slates
`` pH (ISO 1148): 8-9
`` Consumption (2 layers): 500-700gr/m2 on cement substrate
1-1,25 kg/m2 for two coats on mineral bitumen membrane
400 g/m2 on metallic surfaces
`` Drying time: 2-3 h (25°C)
`` Dry to recoat: 24 h (25°C)
`` Solar Reflectance (SR%): 91,8% (Visible: 400-750 nm)*
`` Total Reflectance (SR%): 88% *
`` Solar Reflectance Index (SRI): 111 (ASTM E1980-01)
`` Total Emittance: 0,86 (ASTM E408-71)

* (ASTM E 903-96), (ASTM G159-98)

Packing: 13kg, 4kg, 1kg plastic container

4
APPLICATION PROCEDURE
Surface preparation Dilute with 5% water for the first coat. Apply the second coat after 24
The substrate should be clean, dry and free from dust, oil, grease, or any hours, without thinning. Follow the above directions for the third layer.
poorly adhering material (pic. 1). In case of application over Neotherm® (pic. 4), apply Neoroof® (pic. 5) af-
ter 24 hours, without priming.
Surface priming For demanding applications or when covering cracks cracks between
It is advisable to prime the surface with Revinex® diluted with water in ra- 1,5-2mm, Neoroof® may be reinforced with specially designed non-wo-
tio Revinex®:water-1:3, in order to seal any pores, fix the surface, and thus ven polyester reinforcement Neotextile® (pic 6). In such cases, at least
obtain stronger adhesion and higher coverage (pic. 2). three coats are required (pic 7).
It is recommended to insulate the vertical surfaces of roofs at least for 20-
Application 30cm (pic. 8) in order to create a continuous waterproofing membrane.
Stir the product thoroughly in its container. After priming, apply at least two In case of application over asphalt membrane, apply 1-2 coats of primer
layers of Neoroof® using a brush or a roller (pic. 3) each time applying in a Revinex® diluted with water in ratio Revinex®:water – 1:3, followed with
vertical or different direction to that of the previous coat. at least 2 layers of Neoroof® coating.

   

   

5
WATERPROOFING OF WALKABLE ROOFS USING CEMENTITIOUS ELASTIC SYSTEM

Neoroof® 2K
Smooth, elastic, 2-components, cementitious waterproofing system
for roofs
It is specially designed to resist UV rays and low temperatures down to -20°C.
It yields a smooth walkable surface.

APPLICATION PROCEDURE
Surface Preparation
Surfaces must be dry, clean from dust, dirt, greasy substances and be
homogeneous (pic. 1). For corrosion protection of reinforcement that
probably will arise, Ferrorep® is recommended (pic.2). Cavities or other
imperfections must be repaired with Neorep® and Revinex® (pic. 3).

Surface Priming
Before applying Neoroof® 2K, priming of surfaces is recommended. To
prime the surfaces use Revinex® mixed with water in a ratio of 1:4. This
way, we achieve a wet and stabilized substrate, on to which Neoroof® 2K
we adhere excellently (pic. 4).

Application of Neoroof® 2K
Gradually add the A component (solid) to the B (liquid) and mix with a low-
rev stirrer (to avoid air entrapment) until it is homogeneous. Do not add
P R O P E R T I E S & A D VA N TA G E S water or other inert materials. If the partial application of the mixture is
necessary, follow the mixing ratio (by weight) 75% A and 25%B. Apply
`` Exhibits increased elasticity the mixture without delay by brush, roller, spatula, preferably in 2 layers
`` It remains elastic down to -20°C of 1 to 1,5mm thickness each, in order to obtain a final thickness of 2 to
`` It is water vapor permeable 3 mm (pic. 5). For thicker coatings and resistance to tearing, (e.g. at up-
`` Provides walkability and it is not affected by UV radiation stands, cracks) use fiberglass mesh Gavazzi® 0059-A (pic. 6), between
`` Certified with CE (EN 1504-2) the 2 coatings, while the 1st is still wet (pic. 7). Never apply when rain is
`` Exhibits great resistance to walkable roofs, even with stagnant water forecasted. Allow to dry between 5 and 8 days, before applying tiles or
`` It has smooth finish other coatings.
`` Environmentally friendly
`` It bridges cracks, pores, joints of small width

F I E L D S O F A P P L I C AT I O N

`` Roofs made of concrete, cement boards, mosaic, cement slurries

`` Rooftops with resistance at stagnant water
  
TECHNICAL CHARACTERISTICS

`` Mixing ratio (by weight): 2,5:1

`` Colour of mixture: grey / off white
`` Indicative consumption: 2-2,5 kg/m2 for 2 layers
`` Pot life: 45 minutes (25°C)  
`` Minimum application temperature: +5°C
`` Drying time: 7 - 8 hours (25°C)

Note: low temperatures during application prolong the setting time, while high tem-
peratures bring it down.

 
Packing: Set of 35 kg and 17,5 kg

6
Neoroof® Nordic
Hybrid waterproofing coating for roofs (UV curable)
Hybrid waterproofing coating for roofs, in terracotta shade, for colder climates, with resistance to extremely
low temperatures down to -35°C. It forms a non-penetrating film against moisture.

P R O P E R T I E S & A D VA N TA G E S APPLICATION PROCEDURE

`` It is applied easily and dries into a smooth film that covers capillary
Surface preparation
cracks and provides total protection against moisture.
The substrate should be clean, dry and free from dust, oil, grease, or any
`` Neoroof® Nordic has a UV cross-linking system incorporated, de-
poorly adhering material.
signed to give very good dirt pick-up resistance. After 2 days exposure
to direct sunlight the film is no tacky even under high temperatures.
Surface priming
`` It is not affected by adverse weather conditions and maintains its elas-
It is advisable to prime the surface with Revinex® diluted with water in ratio
ticity for temperatures down to -35°C, offering excellent impermeabil-
Revinex®:water-1:3 up to 1:4, in order to seal any pores, fix the surface, and
ity to water.
thus obtain stronger adhesion and higher coverage.

Application of Neoroof® Nordic

F I E L D S O F A P P L I C AT I O N Stir the product thoroughly in its container. After priming, apply at least two
layers of Neoroof® Nordic using a brush or a roller, each time working the
`` Roofs made of concrete, cement boards, mosaic, cement slurries material in a vertical or different direction to that of the previous coat. Dilute
`` Rooftops with resistance to stagnant water with 5% water for the first coat. Apply the second coat after 24 hours, with-
`` Mineral bitumen membranes out thinning. Follow the above directions to the third layer.
`` Metallic surfaces In case of application over bitumen membranes with gravel stone, apply 1-2
`` New or old polyurethane waterproofing layers coats of primer Revinex® diluted with water in a ratio of Revinex®: water –
`` Thermal-insulating polyurethane panels and polycarbonate panels 1:3. Then apply at least 2 layers of coating Neoroof® Nordic.
`` Glass surfaces
`` Galvanized metal sheets and bituminous membranes with aluminium
sheet surface
`` Over old roofing made of asbestos
(Upon some surfaces above, it is necessary to prime them with the appropriate
each time primer, before Neoroof® Nordic application)

TECHNICAL CHARACTERISTICS

`` Appearance: viscous liquid-terracotta

`` Density (ISO 8962): 1,31 g/cm3
`` Consumption: 500-700gr/m­2 for two coats (cementitious surface)
`` Drying time: 2-3 h initially
`` pH (ISO 1148): 8-9
`` Dry to recoat: 24 h
(low temperatures and high humidity prolong drying)

Packing: 13 kg and 4kg plastic containers

7
WATERPROOFING OF UNDERGROUND WALLS
WATERPROOFING OF UNDERGROUND WALLS WITH CRYSTALLINE CEMENTITIOUS MORTAR

Neopress® & Revinex®

Pre-mixed mortar of crystalline action, based on cement
for the construction of waterproof coatings
Brushable cementitious 2-component waterproofing system (5:1), for the creation of water-
proofing coatings. It is advised to add Revinex® (up to 20%). It shows remarkable resistance
to positive and negative hydrostatic pressure.

P R O P E R T I E S & A D VA N TA G E S APPLICATION PROCEDURE

`` Fills and seals the pores of the surface and thus offers total impermeability Surface preparation and priming
to water and protection against corrosion
The substrate should be clean, free from dust, greasy or oily substances,
`` Resistant to positive and negative hydrostatic pressure and bridges cracks
poorly adhering material, and should be sufficiently damp. For anticorro-
and cavities
sive protection of the reinforcement, apply Ferrorep® (pic. 1). The surfac-
`` For applications that demand very high water impermeability (e.g. water
es should be wet or even better be primed with a mixture of Revinex +
tanks), it is suggested to add Revinex® up to 20%, which offers increased
water 1:1 (pic. 2). Cavities or other imperfections must be repaired with
elasticity and durability in time.
Neorep® (pic.3).
`` Neopress® has been shown to provide excellent durability and imperme-
ability to water (EN 934-3)
Application of Neopress®/Revinex®
`` CE certification (EN 1504-2)
Dilute 5 kg Revinex® with 5 kg water and gradually add 25 kg Neo-
`` Long shelf life thanks to plastic packing
press® under continuous and intense agitation with a mechanical stir-
rer until the slurry is homogeneous. Apply the mixture using a brush or
roller without delays, at a thickness of 1 - 1,5mm for each layer (pic.
F I E L D S O F A P P L I C AT I O N
4). For thicker coatings and resistance to tearing, (e.g. at upstands,
`` Waterproof coatings of underground rooms and basements, tunnels, cracks) use fiberglass mesh N-Thermon® mesh 90gr (pic. 5), between
walls, water tanks, wells, jardinières the 2 coatings, while the 1st is still wet (pic. 6). In cases where negative
`` Concrete, mortar, bricks, concrete blocks, mosaic pressure is high (such as basement interiors), prepare a priming layer
by diluting Neopress® in water by 30%. Then apply two more layers
as described above. In case of lower demands, when less Revinex® is
TECHNICAL CHARACTERISTICS needed, should keep the ratio 2.5:1 between solid-liquid, e.g. 1,5 kg
Revinex® with 3,5 kg water and gradually add 12,5 kg Neopress® un-
`` Tensile strength: 3,63 MPa (28 days DIN 53504) der continuous and intense agitation with a mechanical stirrer until the
`` Elongation at break: 3,13% (28 days DIN 53504*) slurry is homogeneous. During the summer or whenever the weath-
`` Compressive strength at 28 days (EN 1015-11): 32,13 Mpa er is hot, it is advisable to dampen the coat after the application of the
`` Resistance to penetration (EN 1015-9): 12,76 MPa mortar to avoid dehydration and crack formation.
`` Water penetration (EN 1015-8): 0,4kg/m2 min 0,5 (class W1)
`` Adhesive strength (EN 1015-12): 0,4N/mm2 (class FPa)
`` Density: 1,30 g/cm3 (for grey colour)
1,24 g/cm3 (for white colour)
`` Admixture colour: white and grey
`` Consumption: 2 kg/m2 (for 2 layers)
* Enriched with Revinex®

Packing:
Neopress® in plastic container of 25kg,
Revinex® in tin containers of 5kg  

   

8
 WATERPROOFING OF UNDERGROUND WALLS
WITH HIGH STRENGTH CEMENTITIOUS MORTAR

Fondaproof®
One component brushable cementitious waterproofing system

P R O P E R T I E S & A D VA N TA G E S APPLICATION PROCEDURE

`` Remarkable adhesion on most building surfaces
Surface preparation and priming
`` Provides waterproofing and resistance to extreme environmental con-
The substrate should be clean, free from dust, oil, grease, or any poorly
ditions
adhering material and moistened soon before application. Imperfections,
`` Resists positive and negative hydrostatic pressure
holes, cavities, etc. should be repaired by using premixed mortar Neo-
`` The addition of the emulsion (Fondaproof® component B) increases
rep®. The use of component B as a primer in order to achieve stabiliza-
the elasticity and the adhesion of the system
tion is optional.
`` Enhanced abrasion resistance and thus produces dust-free coats
`` CE certification (EN 1504-2)
Application of Fondaproof
`` It is economic and easy to apply even by non specialized personnel
Add gradually component A (powder) to the proper quantity of water (~7kg)
or to the liquid component B (pic 1, 2) and mix using a low speed mechanical
F I E L D S O F A P P L I C AT I O N mixer to avoid air being dragged into the mix. Keep stirring until a perfectly ho-
mogeneous mix is obtained (pic. 3). The junction of wall-floor is applied with
`` Underground rooms, walls, jardinières Fondaproof® in two layers reinforced with fiberglass N-Thermon® mesh
`` Masonry surfaces, concrete, cement mortars, lime-cast, bricks, stone- 90gr between the 2 layers (pic. 4, 5).
work, etc. As soon as the mix is homogeneous, start applying it by using a brush, in
`` It is applied easily on exterior walls, basement floors and foundations, re- two layers (pic. 6). The second layer should be applied vertically to the first
taining walls, bathrooms, wells, jardinieres, tunnels etc. and surfaces un- one (pic. 7). For more coats, the use of fiberglass Gavazzi® 0075-A is rec-
der ceramic tiles. ommended (pic. 8). Fondaproof® component A can be applied also as a
single component with the addition of water only, in cases waterproofing
demands are not high.
TECHNICAL CHARACTERISTICS

`` Mixing ratio: A:B=25:7

`` Admixture Colour: grey
`` Drying time: 1-2 hours (20°C)
`` Time of workability: 3 hours (20°C)
`` Minimum application temperature: 8°C
`` Consumption: 2-3 kg/m2 for two layers  
Packing: 25 kg carton bags

 

   

9
WATERPROOFING OF FACADES
WATERPROOFING OF VERTICAL SURFACES USING WATERPROOFING
COATINGS WITH THERMAL INSULATING PROPERTIES

Silatex® Reflect
Reflective, elastomeric waterproofing paint with heat insulating properties

P R O P E R T I E S & A D VA N TA G E S APPLICATION PROCEDURE

`` It reduces the temperature of the exterior surface exposed to the sun
Surface Preparation
and offers cool conditions at summer time
Surfaces must be dry, clean from dust, dirt, greasy substances. Before the
`` Water vapor-permeable, allowing walls to breath. It retains its elasticity
application, for stabilizing the surface, sealing all pores, enhancement of
offering waterproofing for many years
the adhesion and the materials’ coverage, apply 1 coating of Revinex® di-
`` Interacts with UV and solar radiation, providing a tack-free surface,
luted with water (Revinex:Water-1:3) or Silatex® Primer diluted 30% with
even at very high temperatures. As a result, it retains its reflective prop-
Neotex® 1111.
erties and the white shade for a long period of time.
`` Covers capillary cracks and completely protects from moisture
Application
`` Resistant at temperatures down to -40°C
Silatex® Reflect is applied after thorough stirring, in at least 2 coatings.
`` Offers high coverage and spreading
Apply it with brush or roller. The first coating is diluted with water (5%). The
second is applied after 24 hours, undiluted.

TECHNICAL CHARACTERISTICS

`` Appearance: White, viscous liquid

`` Specific Gravity: 1,36 g/cm3
`` Consumption: 0,18-0,20 L/m2
`` Touch dry: 3 hours (25°C)
`` Dry to recoat: 24 hours (25°C)
`` Solar Reflectance (SR%): 91% (400-750 nm)*
`` Total Reflectance (SR%): 88 (300-2400 nm)*
`` Solar Reflectance Index (SRI): 111 (ASTM E1980-01)
`` Infrared Emmitance coefficient (ε): 0,86 (ASTM E408-71)
* (ASTM E 903-96), (ASTM G159-98)

- CRES- Laboratory for Energy Tests

- University of Athens

Packaging: 10 L and 3 L plastic containers

10
Revinex® Flex 2006
Elastic cementitious waterproofing system
Elastic cementitious 2-component system (2,4:1) for the creation of elastic watertight coatings
on surfaces that undergo contractions-expansions or vibration.

P R O P E R T I E S & A D VA N TA G E S APPLICATION PROCEDURE

`` Offers high elasticity, impermeability and protection to every vertical or
Surface preparation
horizontal construction surface, that is subjected to vibrations, contrac-
Surfaces must be dry, clean from dust, dirt, greasy substances and ho-
tions – expansions or chemical substances
mogeneous (pic. 1). Cavities or other imperfections must be repaired with
`` Remarkable adhesion on numerous substrates, like concrete, cement
Neorep® (and Revinex®).
slurries, bricks, metals, gypsum boards, polysterene, mosaic and ceramic
`` Certified for application at tanks with potable water Surface priming
`` Prevents metallic reinforcements corrosion, while enhances adhesion Non-porous surfaces must be dry, while porous should be wet (until satu-
of cement on to the reinforcement ration), or even better be primed with a mixture of Revinex® + water (ratio
`` Resistant at low temperatures and snow/frost melting 1:1), removing the excess water before application.
`` Water vapor-permeable, protects from concrete carbonization
`` Certified with CE (EN 1504-2) Application of Revinex® Flex 2006
`` Resistant to positive and negative hydrostatic pressure Gradually add the A component (solid) to the B (liquid) and mix with a low-
`` Economic and easy to apply, even from un-trained personnel rev stirrer (to avoid air entrapment) until it is homogeneous. Do not add
`` Bridges cracks, pores and thin joints water or other inert materials. If the partial application of the mixture is
`` Protects from underground radon and chloride migration necessary, follow the mixing ratio of 70%Α and 30% Β.
`` Environmentally friendly
`` Compatible with previous waterproofing layers Application
Apply the mixture without delay by brush, roller, spatula, preferably in 2
layers of 1 to 1,5mm thickness each (pic. 2). For thicker coatings and resis-
F I E L D S O F A P P L I C AT I O N tance to tearing, (e.g. at upstands, cracks) use fiberglass mesh Gavazzi®
0059-A (pic. 3), between the 2 coatings, while the 1st is still wet (pic. 4).
`` Surfaces under tiles in swimming pools, balconies, rooms, bathrooms, Never apply when rain is forecasted. Allow Revinex® Flex 2006 to dry be-
kitchens tween 5 and 8 days, before applying tiles or other coatings (pic. 5).
`` Shafts, water tanks (also potable water), jardinières, silos
`` Underground surfaces of buildings, interior or exterior
`` Tunnels and motorway bridges

TECHNICAL CHARACTERISTICS

`` Surpasses the requirements of EU Norm ΕΝ 934-3, table 3

`` Compressive strength (EN 1015-11/99): 14,0Mpa
`` Flexural strength (EN 1015-11/99): 4,1 Mpa
 
`` Resistance to penetration (EN 1015-09): 18,43Ν/mm2
`` Tensile strength (28 days DIN 53504*): 9,61Ν/mm2
`` Elongation at break (28 days DIN 53504): 16,8%
`` Mixing ratio (By weight): 70%Α-30%Β or 2,4:1
`` Color: grey
`` Indicative consumption: 2-2,5kg/m2 for 2 layers
`` Pot life: 30’
 
`` Minimum application temperature: +5οC
`` Drying time of each layer: 8 - 10 h
Note: these times are prolonged by low temperatures and moisture, while short-
ened by higher ones.
*with fiberglass mesh Gavazzi® 0059-A

Packing: Set of 34kg, 17kg  

11
AUXILIARY PRODUCTS

Revinex® Neorep®
Multi-purpose co-polymeric emulsion, that, ow- High strength fibre reinforced non-shrinking ce-
ing to its compatibility with cementitious aggre- mentitious mortar for repair jobs on concrete
gates, it offers waterproofing, adhesion, elasticity elements. Highly thixotropic and meets the re-
to numerous repairing jobs. quirements of Class R4 of EN 1504-3.
Dosage: 1-5kg per cement bag 50kg according Packing: 25kg carton bags and 5kg plastic con-
to application field and required final properties tainers
Packing: 1kg, 5kg and 18kg tin containers and
200kg drums

Neocret®
High strength fiber-reinforced cementitious mor-
tar for repair jobs on concrete.
Neotherm® Consumption of fresh mix: 1,8 Kg/m2/mm
Packing: 25kg carton bags and 5kg plastic con-
High quality thermal insulating material for
tainers
roofs and facades under waterproofing coat-
ings Neoroof® and Silatex® Reflect
Consumption: 0,5-0,7 L/m2
Packing: 10 L and 3 L in plastic containers
Gavazzi® 0059-A
Alkaline-resistant fiber glass mesh 61gr/m2 with
mesh width 2,7 x 2,7 mm.
Applications: coatings, cementitious waterproof-
ing systems. Doesn't rot or rust over time and it

Neotextile®
is easily applied due to significantly lower weight
and its flexibility.
Non-woven polyester reinforcement 60gr/m2 Packing: Rolls of 50x1m
suitable for reinforcement of coatings. It does not
require great consumption of coatings for its im-
pregnation. Specially recommended for covering
cracks and upstands.
Packing: Rolls of 300m, 100m, 50m x 1,08m N-Thermon® mesh
90gr
Alkaline-resistant fiber glass mesh 90gr/m2 with
mesh width 4,0 x 5,0 mm. Applications: coat-
ings, cementitious waterproofing systems and

Ferrorep®
mortars.
Applications: coatings, cementitious water-
Cement based anticorrosive coating with CE cer- proofing systems.
tification (EN 1504-7) for steel reinforcement of Packing: Rolls of 50x1m
concrete elements. Strong bonding old to new
concrete. Very strong adhesion on metals. Dura-
bility against extreme weather conditions.
Consumption: 50-70 gr per linear meter of rein-
forcement element for 2 layers of total thickness
of 1mm
Packing: 20kg, 4kg, 1kg plastic containers

12
OTHER WATERPROOFING PRODUCTS

Waterproofing Neostop®
Extremely fast-setting fixing cement for instant
sealing of water-leaking or moist spots.
Neotex® Silimper Packing: 5kg plastic containers

Waterproofing silicone-based impregnating ma-

terial for the protection of exterior surfaces of
buildings. Suitable for vertical (or inclined) porous
Epoxol® Putty
building surfaces, such as concrete, plasters and Two-component bonding-sealing system based
renderings, asbestos cement, limestone, brick, on epoxy resins & hardener. Applied in cases
roof tiles, marble, stone with continuous surface that demand resistance to thermal and mechani-
(i.e. without cracks). cal stress, corrosive agents and impermeability to
Consumption: 0,2-0,33L/m2 water. Strong bonding of metals, concrete, wood,
Packing: 1L, 4kg and 17kg tin cans ceramics, building materials, heat insulating tiles,
polyester, hard plastics (e.g. PVC).
Packing: Set of 20kg, 6kg, 1kg
Betofix® Waterstop
Durable solvent-based paint for the protection
of moist surfaces made of mortars or concrete,
Jointex®
in basements, walls and air-conditioned rooms Elastomeric acrylic mastic for sealing joints and
where the presence of moisture is obvious. openings. Joints in concrete, glass, roof tiles, an-
Diluted with Neotex® 1111. odized aluminum, wood, etc. Maintains its elastic-
Consumption: 500gr/m2 ity in a wide range of temperatures. Shows very
Packing: 1kg, 5kg tin cans good adhesion to many substrates. Can be recoat-
ed with any water-based paint, resistant to weath-
ering and ultraviolet radiation. Stable in areas with
Neoproof® industrial atmosphere & fumes. Resistant to ex-
ceedingly diluted acids, bases and detergents.
Water-based elastomeric compound with excep- Colors: White and terracota
tional elasticity (>500%) for interior use. Suitable Packing: 15kg plastic containers (white),
for water tanks, jardinières or floors that will be 5kg and 1kg plastic containers (white and terracota)
covered with tiles, bathrooms, kitchens, gypsum
boards, underground walls, basements beneath
ground level, water barrier or vapour barrier before
the placement of thermo-sound insulation plates. Thermal Insulation
Colors: Beige.
Consumption: 1 m2/kg for 2 layers
Packing: 1kg, 5kg and 22kg plastic containers N-Thermon® System
Innovative thermal insulating boards of extruded
polystyrene hard foam, of small thickness 6 and
9mm, without CFC (freon). Can be painted with
Sealing - Bonding a premium quality interior water-based paint, or
covered with ready to use mortar Deplast®.
Dimensions: 1,25 x 0,80m
Neotex® PU Joint
Polyurethane elastomer, suitable for sealing joints
& openings in concrete, glass, anodized alumi-
num, wood, etc.
Neotherm® AC
Coverage per 600ml sausage: Certified, heat insulating, anti-condensation coat-
6m joint 10 x 10mm / 24m joint 5mm x 5mm ing for interior walls. Ideal as the final coating over
Packing: 600ml, 310ml N-Thermon® thermal insulation system.
Packing: 10 L, 3 L plastic containers

13
 Indicative applications of NEOTEX® waterproofing systems

Bank of Georgia, Tbilisi, Georgia New Urban Planning Building, Taneco Oil Refinery, Kazan, Tatarstan
Nicosia, Cyprus

Kozya Sloboda Metro Station, Volgograd Shipping Lock, Russia Stadium Qemal Stafa, Tirana, Albania
Kazan, Tatarstan

Kempinski Hotel, Sofia, Bulgaria Tbilisi Mall, Tbilisi, Georgia Kvareli Lake Resort, Georgia

Ostankino TV Tower, Moscow, Russia Hotel Zabljak, Montenegro Residential-Building, Bucharest, Romania

14
 WATERPROOFING & INSULATION

Waterproofing
Cementitious Waterproofing Systems Insulation & Energy Saving Repairing Materials
Field of Coatings
application
Revinex® Flex Neopress® N-Thermon® Neoroof® Neotex® Neotex®
Neoroof® 2K Fondaproof® Neotherm® Neotherm® AC Neoroof® Silatex® Reflect Neostop® Epoxol® Putty Jointex®
2006 & Revinex® 6 & 9 mm Nordic Silimper PU-Joint

Roofing ü ü
Under hybrid Resistant to stag- ü
ü waterproof- nant water and
ü For joints and
   ü Under tiles appli- ü For cracks and
ing coating Ne- adverse weath- openings up
cations joints
oroof®, Silatex® er temperatures to 5cm
Reflect and UV

Thermal ü
insulation
ü
ü ü ü High reflection & High reflection &
emittance emittance

Bathroom
& kitchens ü ü ü ü ü ü ü ü ü

Interior walls ü ü ü ü ü ü ü ü ü
Underground ü ü ü ü ü ü ü
Jardinières ü ü ü
Tanks ü
Certified for drinks ü ü ü
water

Pools ü
Before epoxy paint- ü ü ü ü
ing or ceramic tiles

Balconies ü
Resistant to vibra-
ü tions. Under ceram-
ü ü ü ü
ic tiles

Porous mate- ü
rials (bricks, ü ü ü ü ü ü In terracotta ü
stones etc) colour

Exterior walls ü
Covers capillary
ü ü cracks. Combined
ü
Applied on fa- Applied on fa- Can be over-
with Neotherm®
ü cades and coat- cades and coat- ü ü painted with ü
provides water-
ed with Silatex® ed with Silatex® water-based
proofing and ther-
Reflect Reflect paints
mal insulation
together

Metallic
surfaces ü ü ü ü ü ü ü

15
 Your confidence...
is not a coincidence!

,gr
Ver. 3 - April 2014

S.A.
ATHENS: V. Moira str., P.O. Box 2315, 19600 Industrial Area Mandra Attikis, Greece, Τel. +30 210 5557579, Fax: +30 210 5558482
THESSALONIKI: 10th km N.R Thessaloniki-Poligiros, 57001, Thermi Thessaloniki, Greece, Tel.:+30 2310 467275, FAX: +30 2310 463442
www.neotex.gr • e-mail: export@neotex.gr

FLOOR PROTECTION - WATERPROOFING - ADMIXTURES - REPAIRING - ENERGY SAVING