Ahwaz Pipe Mills Test Certificate Quality Control Laboratory

This document is a test certificate from Ahvaz Pipe Mills Quality Control Laboratory. It provides testing results for the environmental stress cracking resistance of triple layer hot extruded polyethylene corrosion coating on pipe. The test was conducted according to specified methods and met requirements with no cracks observed after 300 hours of testing.

Uploaded by

stdshop
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as XLS, PDF, TXT or read online on Scribd
88 views2 pages

Ahwaz Pipe Mills Test Certificate Quality Control Laboratory

This document is a test certificate from Ahvaz Pipe Mills Quality Control Laboratory. It provides testing results for the environmental stress cracking resistance of triple layer hot extruded polyethylene corrosion coating on pipe. The test was conducted according to specified methods and met requirements with no cracks observed after 300 hours of testing.

Uploaded by

stdshop
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as XLS, PDF, TXT or read online on Scribd
You are on page 1/ 2

APM NO. : Contract No.

AHWAZ PIPE MILLS


APMP NO . : TEST CERTIFICATE Specification :

QUALITY CONTROL LABORATORY


Size & Grade : Date :

THREE LAYER HOT EXTRUDED PE. CORROSION COATING


Material Supplier : Report - Part No :

ENVIRONMENTAL STRESS CRACKING RESISTANCE ( PE ) Sort by Batch


Customer : Page / Part No. :

ITEM BATCH DATE OF


RESULT REMARKS
NO. No. TEST
TYPE OF PE :

TYPE OF COAT :

COLOR OF PE :

MIN. THICK. OF COATING :

FREQUENCY OF TEST :

TEST METHOD :

EXPOSURE TIME :

DIMENSION OF TEST SPECIMEN :

NOTCH DEPTH :

CONSTANT-TEMPERATURE BATCH :

TEST TUBE :

REAGENT :

REQUIREMENT : No CRACK AFTER 300 HOURS

K.KALANTARIAN A.H.Bossagh Zadeh CUSTOMER INSPECTION :


HEAD OF LAB. : HEAD OF Q.C. :
QC/LAB/P16 / 16 REV.: 03 Date 08.2002